The effects of fiber diameter and molecular weight of the matrix polymer in glass fiber reinforced polypropylene composites have been investigated on the interfacial microstructure. The influences of the surface state of fiber and the heat treatment condition on the interfacial morphology and the spherulitic formation process in matrix have also been investigated. From this study, it has been found that both fiber diameter and molecular weight of the polymer significantly influence the thickness of the transcrystalline layer. In addition, the radius of the largest spherulites in matrix has been found to be about the same as the thickness of transcrystalline region and to largely depend on the holding time at the crystallization temperature and cooling condition(or rate).

유리섬유강화 열가소성 수지 복합재료의 계면거동 및 기계적 성질에 대한 연구의 일환으로 섬유직경이 다른 유리섬유와 분자량이 다른 polypropylene(isotactic)을 사용하여 유리섬유와 PP matrix의 계면조직에 섬유직경과 matrix의 분자량이 미치는 영향을 Hot stage와 편광현미경을 이용하여 검토하였다. 그 결과 polypropylene의 분자량 및 유리섬유의 섬유직경은 섬유축을 따라 형성되는 관상모양의 transcrystallinity의 morphorlogy에 영향을 미치며 matrix의 구정의 반경과 transcrystallinity의 두께는 같은 것을 알았다. 그리고 열가소성 복합재료에서 transcrystallinity의 형성은 matrix에서 구정의 형성과 성장을 억제한다.

Keywords: